A Ti-49.5 at. % Ni alloy was deformed under isothermal conditions in the temperature range of the B2 → R → B19' martensitic transformations, and the resistivity of the alloy was measured concurrently. It was established that the effects of stress and temperature on the martensitic transformation in the alloy are not equivalent.