The present work has studied electrochemical and optical properties of poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) film electrodes drop-casted from commercial PEDOT:PSS aqueous dispersion with preliminary addition and without addition of LiClO₄ electrolyte (further denoted as PEDOT:PSS/LiClO₄ and PEDOT:PSS). Cyclic voltammetry measurements showed the significant increase in capacitance of PEDOT:PSS/LiClO₄ film electrodes in comparison to PEDOT:PSS. Furthermore, the improved charge transport in PEDOT:PSS/LiClO₄ films was demonstrated by electrochemical impedance spectra. In situ spectroelectrochemical measurements revealed that preliminary addition of LiClO₄ into PEDOT:PSS aqueous dispersion allows to increase amount of free charge carriers (polaron and bipolaron states) in the resulting film during electrochemical oxidation in LiClO₄ propylene carbonate solution. This increase was attributed to ion-induced charge screening between positively charged PEDOT and negatively charged PSS in polyelectrolyte structure, which was supported by structural investigations of both types of film electrodes by using FTIR, SEM, and XPS measurements. Charge screening results from a more open structure that allows conformational relaxation of PEDOT molecules during charge transport, which leads to partial separation of oppositely charged PSS and PEDOT molecules and facilitating the increase of electrochemical activity. [Figure not available: see fulltext.]