This work presents the study of an influence of ultrafine-grained (UFG) structure on impact toughness and dynamic compression of commercially pure titanium Grade 4. The UFG structure was provided by means of equal-channel angular pressing according to the Conform scheme (ECAP-Conform, Ufa) with subsequent heat treatment. Impact toughness tests on samples with U-shaped notch were carried out using a drop weight impact machine. Dynamic compression test of cylindrical samples were carried out on a setup with the Split-Hopkinson pressure bar (SHPB-20) by the Kolsky method. It was found that the impact toughness of the UFG titanium is 15% greater than that of its coarse-grained (CG) counterpart. However, fracture process of the CG material requires 1.5 times more energy. The ECAP treatment significantly increased yield strength of the material. At the same time, an increase of compression strain rate by 6 orders resulted in an increase of yield strength of the CG material by 20%, while yield strength of the UFG titanium remained at the level of a quasi-static load. The UFG material showed a well-expressed strain hardening behaviour for all strain rates.