This paper studies the effect of equal channel angular pressing-Conform (ECAP-C) and further artificial aging (AA) on microstructure, mechanical, and electrical properties of Al 6101 alloy. As is shown, ECAP-C at 130 °C with six cycles resulted in the formation of an ultrafine-grained (UFG) structure with a grain size of 400-600 nm containing nanoscale spherical metastable β′ and stable β second-phase precipitates. As a result, processed wire rods demonstrated the ultimate tensile strength (UTS) of 308 MPa and electrical conductivity of 53.1% IACS. Electrical conductivity can be increased without any notable degradation in mechanical strength of the UFG alloy by further AA at 170 °C and considerably enhanced by additional decomposition of solid solution accompanied by the formation of rod-shaped metastable β′ precipitates mainly in the ultrafine grain interior and by the decrease of the alloying element content in the Al matrix. It is demonstrated that ECAP-C can be used to process Al-Mg-Si wire rods with the specified UFG microstructure. The mechanical strength and electrical conductivity in this case are shown to be much higher than those in the industrial semi-finished products made of similar material processed by the conventional T6 or T81 treatment.