Структурно-фазовое состояние металла рельса с внутренней трещиной после длительной эксплуатации. / Атрошенко, Светлана Алексеевна; Майер, Сергей Сергеевич; Смирнов, Владимир Игоревич.
In: ЖУРНАЛ ТЕХНИЧЕСКОЙ ФИЗИКИ, Vol. 91, No. 9, 09.2021, p. 1363-1368.Research output: Contribution to journal › Article › peer-review
}
TY - JOUR
T1 - Структурно-фазовое состояние металла рельса с внутренней трещиной после длительной эксплуатации
AU - Атрошенко, Светлана Алексеевна
AU - Майер, Сергей Сергеевич
AU - Смирнов, Владимир Игоревич
PY - 2021/9
Y1 - 2021/9
N2 - During operation, under cyclic force action, various physical and mechanical processes occur over time in the rail metal: plastic deformation of the rolling surface, the formation of internal and surface cracks, a change in residual stresses, etc. As a result, the mechanical characteristics deteriorate and the performance of the rails decreases. In this work, a microstructural analysis of the cross-sectional surface of two rails with internal cracks - longitudinal and transverse. Rail samples were taken out of service after many years of service. Fractographic analysis of the crack surface and the surrounding material indicates a significant degradation of the physical and mechanical properties of rail steel.
AB - During operation, under cyclic force action, various physical and mechanical processes occur over time in the rail metal: plastic deformation of the rolling surface, the formation of internal and surface cracks, a change in residual stresses, etc. As a result, the mechanical characteristics deteriorate and the performance of the rails decreases. In this work, a microstructural analysis of the cross-sectional surface of two rails with internal cracks - longitudinal and transverse. Rail samples were taken out of service after many years of service. Fractographic analysis of the crack surface and the surrounding material indicates a significant degradation of the physical and mechanical properties of rail steel.
KW - РЕЛЬСОВАЯ СТАЛЬ
KW - МЕТАЛЛОГРАФИЯ
KW - УСТАЛОСТНАЯ ТРЕЩИНА
KW - МИКРОСТРУКТУРА МЕТАЛЛА
KW - ПОВЕРХНОСТЬ РАЗРУШЕНИЯ
UR - https://journals.ioffe.ru/articles/51215
UR - https://elibrary.ru/item.asp?id=46470753
M3 - статья
VL - 91
SP - 1363
EP - 1368
JO - ЖУРНАЛ ТЕХНИЧЕСКОЙ ФИЗИКИ
JF - ЖУРНАЛ ТЕХНИЧЕСКОЙ ФИЗИКИ
SN - 0044-4642
IS - 9
ER -
ID: 86445117