A method of differential scanning calorimetry has been used for the study of variation in the kinetics of thermal elastic martensitic transformation during the thermal cycling of the equiatomic TiNi alloy through the different fractions of forward or reverse martensitic transformation temperature ranges. The results of the study have shown that "partial cooling" cycling results in damage to the crystalline structure in "transforming" and "austenite" volumes independently of whether or not "austenite" volumes undergo martensitic transformation during partial cycling. The structure damage in "martensite" volumes does not occur during "partial heating" cycling. It is caused by the fact that internal stresses relax through plastic strain in the austenite phase, resulting in an increase in defect density or the reorientation of martensite crystals in the martensite phase without the accumulation of defects. (C) 2014 Elsevier B.V. All rights reserved.
Язык оригиналаанглийский
Страницы (с-по)46-52
ЖурналThermochimica Acta
Том582
DOI
СостояниеОпубликовано - 2014

Fingerprint

Подробные сведения о темах исследования «Variation in kinetics of martensitic transformation during partial thermal cycling of the TiNi alloy». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать