The strength and stability of nanoplates with holes and inclusions

Результат исследований: Материалы конференцийматериалынаучнаярецензирование

Выдержка

The stability problems of thin plates with different defects such as holes, inclusions and cracks under tension are investigated. Loss of planar form of deformation occurs due to the formation of compressive stress zones near defects. By the study of deformation and stability of plates of nanometer thickness should be taken into account the effect of surface stresses acting on the faces of the plate. With the decrease of thickness the surface stresses they could significantly change the bending stiffness of the plate and correspondingly the critical load at which the planar shape of deformation is lost. In this work we study the following problems of stability of thin plates under tension: the plate with circular hole, the infinite plate with circular inclusion, the ring-shaped plate, which is expanded of external forces, the infinite plate with the system of parallel cracks. The analytical results are compared with results of finite element modeling.

Язык оригиналаанглийский
Страницы793-794
Число страниц2
СостояниеОпубликовано - 1 янв 2017
Событие14th International Conference on Fracture, ICF 2017 - Rhodes, Греция
Продолжительность: 18 июн 201720 июн 2017

Конференция

Конференция14th International Conference on Fracture, ICF 2017
СтранаГреция
ГородRhodes
Период18/06/1720/06/17

Отпечаток

Cracks
Defects
Compressive stress
Loads (forces)
Stiffness

Предметные области Scopus

  • Городское и структурное проектирование
  • Строительство

Цитировать

Bochkarev, A. O., Morozov, N. F., Semenov, B. N., & Solovyev, A. S. (2017). The strength and stability of nanoplates with holes and inclusions. 793-794. Документ представлен на 14th International Conference on Fracture, ICF 2017, Rhodes, Греция.
Bochkarev, A. O. ; Morozov, N. F. ; Semenov, B. N. ; Solovyev, A. S. / The strength and stability of nanoplates with holes and inclusions. Документ представлен на 14th International Conference on Fracture, ICF 2017, Rhodes, Греция.2 стр.
@conference{e2c32084ffd8449da26edc44fcbaead1,
title = "The strength and stability of nanoplates with holes and inclusions",
abstract = "The stability problems of thin plates with different defects such as holes, inclusions and cracks under tension are investigated. Loss of planar form of deformation occurs due to the formation of compressive stress zones near defects. By the study of deformation and stability of plates of nanometer thickness should be taken into account the effect of surface stresses acting on the faces of the plate. With the decrease of thickness the surface stresses they could significantly change the bending stiffness of the plate and correspondingly the critical load at which the planar shape of deformation is lost. In this work we study the following problems of stability of thin plates under tension: the plate with circular hole, the infinite plate with circular inclusion, the ring-shaped plate, which is expanded of external forces, the infinite plate with the system of parallel cracks. The analytical results are compared with results of finite element modeling.",
author = "Bochkarev, {A. O.} and Morozov, {N. F.} and Semenov, {B. N.} and Solovyev, {A. S.}",
year = "2017",
month = "1",
day = "1",
language = "English",
pages = "793--794",
note = "14th International Conference on Fracture, ICF 2017 ; Conference date: 18-06-2017 Through 20-06-2017",

}

Bochkarev, AO, Morozov, NF, Semenov, BN & Solovyev, AS 2017, 'The strength and stability of nanoplates with holes and inclusions' Документ представлен на, Rhodes, Греция, 18/06/17 - 20/06/17, стр. 793-794.

The strength and stability of nanoplates with holes and inclusions. / Bochkarev, A. O.; Morozov, N. F.; Semenov, B. N.; Solovyev, A. S.

2017. 793-794 Документ представлен на 14th International Conference on Fracture, ICF 2017, Rhodes, Греция.

Результат исследований: Материалы конференцийматериалынаучнаярецензирование

TY - CONF

T1 - The strength and stability of nanoplates with holes and inclusions

AU - Bochkarev, A. O.

AU - Morozov, N. F.

AU - Semenov, B. N.

AU - Solovyev, A. S.

PY - 2017/1/1

Y1 - 2017/1/1

N2 - The stability problems of thin plates with different defects such as holes, inclusions and cracks under tension are investigated. Loss of planar form of deformation occurs due to the formation of compressive stress zones near defects. By the study of deformation and stability of plates of nanometer thickness should be taken into account the effect of surface stresses acting on the faces of the plate. With the decrease of thickness the surface stresses they could significantly change the bending stiffness of the plate and correspondingly the critical load at which the planar shape of deformation is lost. In this work we study the following problems of stability of thin plates under tension: the plate with circular hole, the infinite plate with circular inclusion, the ring-shaped plate, which is expanded of external forces, the infinite plate with the system of parallel cracks. The analytical results are compared with results of finite element modeling.

AB - The stability problems of thin plates with different defects such as holes, inclusions and cracks under tension are investigated. Loss of planar form of deformation occurs due to the formation of compressive stress zones near defects. By the study of deformation and stability of plates of nanometer thickness should be taken into account the effect of surface stresses acting on the faces of the plate. With the decrease of thickness the surface stresses they could significantly change the bending stiffness of the plate and correspondingly the critical load at which the planar shape of deformation is lost. In this work we study the following problems of stability of thin plates under tension: the plate with circular hole, the infinite plate with circular inclusion, the ring-shaped plate, which is expanded of external forces, the infinite plate with the system of parallel cracks. The analytical results are compared with results of finite element modeling.

UR - http://www.scopus.com/inward/record.url?scp=85066014496&partnerID=8YFLogxK

M3 - Paper

SP - 793

EP - 794

ER -

Bochkarev AO, Morozov NF, Semenov BN, Solovyev AS. The strength and stability of nanoplates with holes and inclusions. 2017. Документ представлен на 14th International Conference on Fracture, ICF 2017, Rhodes, Греция.