The influence of neutron irradiation on the amorphous Ti 40.7 Hf 9.5 Ni 44.8 Cu 5 and Ti 50 Ni 25 Cu 25 thin ribbons, their crystallization behaviour and martensitic transformations that occur after crystallization have been studied. The critical fluence value of 1⋅10 19 cm −2 was found. If the fluence was 1⋅10 19 cm −2 or less, the crystallization parameters and the temperatures of the martensitic transformation that took place alloy after crystallization hardly changed. Otherwise, a huge increase in the crystallization temperature and enthalpy occurred and the degradation of the martensitic transformation in crystallized samples was observed.