The effect of tungsten on microstructure and mechanical performance of an ultrafine Fe-Cr steel

A. Mazilkin, M. M. Abramova, N. A. Enikeev, I. V. Lomakin, R. Z. Valiev, Yu Ivanisenko, C. Kübel, A. Etienne, X. Sauvage, B. Radiguet

Результат исследований: Научные публикации в периодических изданияхстатья

4 Цитирования (Scopus)


Model Fe-Cr alloys with and without W were nanostructured by severe plastic deformation at 350˚C. Transmission electron microscopy observations of the microstructure indicate that the addition of 1 wt% of W led to a reduction of the mean grain size from 129 to 110 nm. Atom probe analyses show that only Cr and Si segregate at grain boundaries during deformation while W remains homogeneously distributed. This solid solution leads to higher mechanical strength and plasticity as compared to Fe-Cr. The origin of the beneficial effect of W on the mechanical performance is discussed.

Язык оригиналаанглийский
Страницы (с-по)292-295
Число страниц4
ЖурналMaterials Letters
СостояниеОпубликовано - 15 сен 2018

Предметные области Scopus

  • Материаловедение (все)
  • Физика конденсатов
  • Сопротивление материалов
  • Общее машиностроение