Simulation of the thermodynamic properties of glass melts in the Cs 2O-B2O3-SiO2 system in the concentration range 0.06-0.50 mole fractions of Cs2O at a temperature of 1020 K

E. N. Plotnikov, V. L. Stolyarova

Результат исследований: Научные публикации в периодических изданияхстатья

1 Цитирования (Scopus)


The possibility of calculating the thermodynamic properties of glass melts in the Cs2O-B2O3-SiO2 system with the use of the vacancy variant of the generalized lattice theory of associated solutions is demonstrated. A comparison with the experimental thermodynamic functions previously determined by high-temperature mass spectrometry shows that the calculations performed within this approach lead to reliable thermodynamic functions for glass melts in the Cs2O-B2O 3-SiO2 system.