Phase Transformations and Thermal Expansion of α- And β-BiTaO4 and the High-Temperature Modification γ-BiTaO4

Nadezhda A. Zhuk, Maria G. Krzhizhanovskaya, Vladimir A. Belyy, Vladislav V. Kharton, Alena I. Chichineva

Результат исследований: Научные публикации в периодических изданияхстатьярецензирование

2 Цитирования (Scopus)

Аннотация

Thermal analysis and X-ray phase analysis under high temperature have defined the order of the BiTaO4 phase transformations in the range of temperature from 25 to 1200 °C: α-BiTaO4 → γ-BiTaO4 → β-BiTaO4 and β-BiTaO4→ γ-BiTaO4 → β-BiTaO4; the new high-temperature phase of bismuth orthotantalate is γ-BiTaO4. It was shown that the transition α-BiTaO4 → β-BiTaO4 is irreversible, in contrast to BiNbO4. The crystal structure of the new bismuth orthotantalate high-temperature modification (γ-BiTaO4) was studied by X-ray powder diffraction. The possible space group of the high-temperature orthorhombic phase was determined as Cmcm, and the parameters of the unit cell were calculated at 900 °C: a = 3.92455(4), b = 15.06243(16), c = 5.63483(6) Å, and V = 333.093(6) Å3. As an alternative, the space group of γ-BiTaO4 was determined as P21/c, and the following unit cell parameters were calculated: a = 7.78151(10), b = 5.63466(6), c = 7.84843(7) Å, β = 104.5858(17)°, and V = 333.033(7) Å3. The method of HTPXRD was used to obtain thermal expansion coefficients (TECs) and to study the thermal deformations of the α, β, and γmodifications of BiTaO4. The average volumetric TECs of all modifications studied had the range of 18.4-33.6 × 10-6 °C-1. The highest anisotropy of thermal expansion was the characteristic of the triclinic phase, β-BiTaO4, whereas α-BiTaO4 had minimal anisotropy and TEC indicating the highest stability of this modification.

Язык оригиналаанглийский
Страницы (с-по)5493-5501
Число страниц9
ЖурналChemistry of Materials
Том32
Номер выпуска13
Ранняя дата в режиме онлайн14 июл 2020
DOI
СостояниеОпубликовано - 14 июл 2020

Предметные области Scopus

  • Химия (все)
  • Химическая технология (все)
  • Химия материалов

Fingerprint

Подробные сведения о темах исследования «Phase Transformations and Thermal Expansion of α- And β-BiTaO<sub>4</sub> and the High-Temperature Modification γ-BiTaO<sub>4</sub>». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать