«Nickel-YSZ-nanoceramics» nanocomposite: Synthesis, structure, and mechanical properties

V. G. Konakov, E. N. Solovyeva, O. Yu Kurapova, N. N. Novik, M. M. Pivovarov, I. Yu Archakov

Результат исследований: Научные публикации в периодических изданияхстатьярецензирование

7 Цитирования (Scopus)

Аннотация

The approach for "nickel-YSZ-nanoceramics" bulk nanocomposite synthesis was developed. Compositions with the nanoceramic phase content lying in the range up to 20 wt.% YSZ were manufactured; their structure and chemical composition were studied using XRD, SEM, and EDX techniques. Experimental study of the composite mechanical properties (compressive strength) as a function of sample composition demonstrated the existence of maximal composite strength at YSZ content of 3 wt.%. Further addition of nanoceramic phase resulted in the significant decrease in material strength.

Язык оригиналаанглийский
Страницы (с-по)340-346
Число страниц7
ЖурналMaterials Physics and Mechanics
Том24
Номер выпуска4
СостояниеОпубликовано - 1 янв 2015

Предметные области Scopus

  • Материаловедение (все)
  • Физика конденсатов
  • Сопротивление материалов
  • Общее машиностроение

Fingerprint

Подробные сведения о темах исследования ««Nickel-YSZ-nanoceramics» nanocomposite: Synthesis, structure, and mechanical properties». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать