Kinetics of isothermal B2 → B19′ martensitic transformation in Ti49Ni51 shape memory alloy

N. Resnina, S. Belyaev, E. Demidova, Алексей Максимович Иванов, Владимир Александрович Андреев

Результат исследований: Научные публикации в периодических изданияхстатья

6 Цитирования (Scopus)

Аннотация

The B2 → B19′ martensitic transformation in a quenched Ni-rich NiTi alloy was found to proceed under isothermal conditions at temperatures both within and outside of the transformation temperature range as observed during continuous cooling measurement. The variation in the volume fraction of the martensite that appeared during isothermal holding of quenched Ni-rich NiTi alloy at different temperatures T was measured. It was found that the maximum volume fraction of the martensite (45%) appeared during holding at Ms temperature for 30 min. It was found that the kinetics of the isothermal transformation was different for T > Ms and T < Ms due to the different structure of the alloy before holding that might influence the mechanisms of the martensite formation.

Язык оригиналаанглийский
Страницы (с-по)348-350
Число страниц3
ЖурналMaterials Letters
Том228
DOI
СостояниеОпубликовано - 1 окт 2018

Предметные области Scopus

  • Материаловедение (все)
  • Физика конденсатов
  • Сопротивление материалов
  • Общее машиностроение

Fingerprint Подробные сведения о темах исследования «Kinetics of isothermal B2 → B19′ martensitic transformation in Ti<sub>49</sub>Ni<sub>51</sub> shape memory alloy». Вместе они формируют уникальный семантический отпечаток (fingerprint).

  • Цитировать