Highly Ordered and Polycrystalline Graphene on Co(0001) Intercalated by Oxygen

Viktor O. Shevelev, Kirill A. Bokai, Anna A. Makarova, Dmitry Marchenko, Oleg Yu. Vilkov, Vladimir Yu. Mikhailovskii, Denis V. Vyalikh, Dmitry Yu. Usachov

Результат исследований: Научные публикации в периодических изданияхстатьярецензирование

Аннотация

We present a comparative study of oxygen intercalation under polycrystalline and highly ordered graphene samples on the Co(0001) surface, which are relevant for magnetic applications. A comprehensive experimental study by means of microscopic and spectroscopic techniques shows that intercalation leads to hole-doping and decoupling of graphene from the strongly bound cobalt surface. However, only for the polycrystalline graphene samples, the full intercalation was achieved. The kinetics of intercalation, graphene etching, and cobalt oxidation has been thoroughly investigated. The obtained results have allowed us to disclose the key points of the oxygen intercalation process for both highly ordered and strongly disordered graphene on cobalt.

Язык оригиналаанглийский
Страницы (с-по)17103-17110
Число страниц8
ЖурналJournal of Physical Chemistry C
Том124
Номер выпуска31
Ранняя дата в режиме онлайн10 июл 2020
DOI
СостояниеОпубликовано - 6 авг 2020

Предметные области Scopus

  • Электроника, оптика и магнитные материалы
  • Энергия (все)
  • Физическая и теоретическая химия
  • Поверхности, слои и пленки

Fingerprint Подробные сведения о темах исследования «Highly Ordered and Polycrystalline Graphene on Co(0001) Intercalated by Oxygen». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать