High-rate performance of LiFe0.4Mn0.6PO4 cathode materials with poly(3,4-ethylenedioxythiopene):poly(styrene sulfonate)/carboxymethylcellulose

R. V. Apraksin, S. N. Eliseeva, E. G. Tolstopjatova, A. M. Rumyantsev, V. V. Zhdanov, V. V. Kondratiev

Результат исследований: Научные публикации в периодических изданияхстатьярецензирование

14 Цитирования (Scopus)

Аннотация

A new cathode material based on C-LiFe0.4Mn0.6PO4 and conducting composite binder poly(3,4-ethylenedioxythiopene):poly(styrene sulfonate)/carboxymethylcellulose (PEDOT:PSS/CMC) was prepared. The obtained composite cathode material containing 96 wt% of C-LiFe0.4Mn0.6PO4 showed the discharge capacity 140 mA h g-1 at 0.2 C and excellent rate capability with discharge capacities of 130 mA h g-1 at 5 C and 118 mA h g-1 at 10 C as well as good cycling stability. The cathode material composition with water-based PEDOT:PSS/CMC binder showed remarkable improvement in high-rate performance with increase of capacity up to 45% at 10 C current density in comparison to that of conventional PVDF-bound electrode.

Язык оригиналаанглийский
Страницы (с-по)248-252
Число страниц5
ЖурналMaterials Letters
Том176
DOI
СостояниеОпубликовано - 1 авг 2016

Предметные области Scopus

  • Материаловедение (все)
  • Физика конденсатов
  • Сопротивление материалов
  • Общее машиностроение

Fingerprint

Подробные сведения о темах исследования «High-rate performance of LiFe<sub>0.4</sub>Mn<sub>0.6</sub>PO<sub>4</sub> cathode materials with poly(3,4-ethylenedioxythiopene):poly(styrene sulfonate)/carboxymethylcellulose». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать