Free volume measurement of severely deformed Zr62Cu22Al10Fe5Dy1 bulk metallic glass

D. V. Gunderov, E. V. Boltynjuk, V. D. Sitdikov, G. E. Abrosimova, A. A. Churakova, A. R. Kilmametov, R. Z. Valiev

Результат исследований: Научные публикации в периодических изданияхстатья в журнале по материалам конференциирецензирование

2 Цитирования (Scopus)

Аннотация

The Zr62Cu22Al10Fe5Dy1 bulk metallic glass (BMG) was subjected to high pressure torsion (HPT) at room temperature and at 150 °C. XRD shows a shift of first amorphous halo towards a low angles, which corresponds to an increase in the first coordination sphere radius and an increase in free volume content approximately by 0.44 % and 0.74 % after HPT processing at temperatures of 20 and 150 °C, respectively. Direct density measurements revealed that HPT at 20 °C and 150 °C leads to a decrease in the density values by 2.1% and 1 %, respectively, in comparison with the initial state. Value of density decrease for state HPT 150 °C estimated by direct density measurements is close to value of free volume increase estimated by shift of first amorphous halo.

Язык оригиналаанглийский
Номер статьи012010
ЖурналJournal of Physics: Conference Series
Том1134
Номер выпуска1
DOI
СостояниеОпубликовано - 5 дек 2018
Событие7th International Conference on Functional Nanomaterials and High Purity Substances, FNM 2018 - Suzdal, Российская Федерация
Продолжительность: 1 окт 20185 окт 2018

Предметные области Scopus

  • Физика и астрономия (все)

Fingerprint Подробные сведения о темах исследования «Free volume measurement of severely deformed Zr<sub>62</sub>Cu<sub>22</sub>Al<sub>10</sub>Fe<sub>5</sub>Dy<sub>1</sub> bulk metallic glass». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать