Accumulation of Residual Strain in TiNi Alloy During Thermal Cycling

Результат исследований: Публикации в книгах, отчётах, сборниках, трудах конференцийстатья в сборнике материалов конференциинаучная

10 Цитирования (Scopus)

Аннотация

Residual strain accumulation during thermal cycling of the Ti50Ni50 alloy under a constant stress of 200 MPa through the temperature range of complete and incomplete forward martensitic transformation was studied. The temperature range of the forward martensitic transformation during thermal cycling was chosen as 25, 50, 75, or 100% of the M (s)-M (f) interval measured in the first cycle. It was shown that intensive accumulation of residual strain took place in the last stage of the forward transformation. It was observed that resistivity increased more rapidly with an increase of the fraction of the temperature range of forward martensitic transformation.
Язык оригиналаанглийский
Название основной публикацииAccumulation of Residual Strain in TiNi Alloy During Thermal Cycling
Страницы2339-2342
DOI
СостояниеОпубликовано - 2014

Fingerprint Подробные сведения о темах исследования «Accumulation of Residual Strain in TiNi Alloy During Thermal Cycling». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать