Название: Structural and electrical properties of n- and p-type silicon and tellurium-doped silicon after 2 MeV electron irradiation
Версия: 1
Ключевые слова:
Аннотация: The formation of the cubic silicon phase (sp.gr. Fd3m) was confirmed in n- and p-type silicon samples, as well as in n- and p-type tellurium-diffused silicon samples annealed for 5 hours. Electron irradiation with fluences of 1×10^15, 1×10^16, and 1×10^17 electrons/cm^2 resulted in changes in the lattice parameters of the cubic silicon phase (sp.gr. Fd3m). While the phase composition of the initial and electron-irradiated samples remained unchanged, irradiation led to noticeable variations in the nanocrystallite size. Hall effect measurements revealed that the resistivity of all samples increased as a function of electron fluence, and the corresponding results were presented. The resistivity of p-type silicon increased from 16.27 to 1042 Ω•cm with increasing electron fluence, while in tellurium-doped p-type samples it increased from 22.40 to 815 Ω•cm. For n-type silicon, the resistivity increased from 15.71 to 594.56 Ω•cm, whereas in tellurium-doped n-type samples it varied from 13.68 to 118000 Ω•cm.
Язык рукописи: English
Авторы:
1) Соавтор:
Имя : Dr Mannab Tashmetov
Сведения о принадлежности автора : Institute of Nuclear Physics of the Academy of Sciences of the Republic of Uzbekistan,Uzbekistan,Tashkent,100214
2) Соавтор:
Имя : Mr Shermakhmat Makhkamov
Сведения о принадлежности автора : Institute of Nuclear Physics of the Academy of Sciences of the Republic of Uzbekistan,Uzbekistan,Tashkent,100214
3) Соавтор:
Имя : Mr Normamat Ismatov
Сведения о принадлежности автора : Institute of Nuclear Physics of the Academy of Sciences of the Republic of Uzbekistan,Uzbekistan,Tashkent,100214
4) Соавтор:
Имя : Mr Nodimjon Sulaymonov
Сведения о принадлежности автора : Institute of Nuclear Physics of the Academy of Sciences of the Republic of Uzbekistan,Uzbekistan,Tashkent,100214
5) Соавтор:
Имя : Mr Sarvar Egamov
Сведения о принадлежности автора : Institute of Nuclear Physics of the Academy of Sciences of the Republic of Uzbekistan,Uzbekistan,Tashkent,100214
6) автор для корреспонденции:
Имя : Mr Abror Abdaminov
Сведения о принадлежности автора : Institute of Nuclear Physics of the Academy of Sciences of the Republic of Uzbekistan,Uzbekistan,Tashkent,100214
7) Соавтор:
Имя : Mr Shavkatjon Nazarmamatov
Сведения о принадлежности автора : Institute of Nuclear Physics of the Academy of Sciences of the Republic of Uzbekistan,Uzbekistan,Tashkent,100214
8) Соавтор:
Имя : Mr Muzaffar Erdonov
Сведения о принадлежности автора : Institute of Nuclear Physics of the Academy of Sciences of the Republic of Uzbekistan,Uzbekistan,Tashkent,100214