Shape Memory Effects and Work Output of [001] Ni55Fe18Ga27 Single Crystals in Torsion Mode

A. Sibirev, S. Belyaev, N. Resnina, R. Timashov, A. Averkin, Владимир Иванович Николаев

Research output

Abstract

The work output of [001] Ni55Fe18Ga27 single crystals was studied under different loading conditions (cooling under 0, 30, 70 and 100 MPa and heating under 150 MPa) in torsion mode. It was shown that during thermal cycling, the functional properties, such as martensitic transformation temperatures, shape memory effect value and work output, of Ni55Fe18Ga27 single crystals stabilized after a few thermal cycles and then barely varied. A maximum work output of 1.15 MJ/m3 was found when the sample was cooled without stress or under a stress of 30 MPa and heated under a stress of 150 MPa. Simultaneously, it was observed that if the stress that was acted on cooling was 30 MPa, then less plastic strain appeared in the sample during thermal cycling.

Original languageEnglish
Pages (from-to)2185-2189
JournalJournal of Materials Engineering and Performance
Volume49
DOIs
Publication statusPublished - 15 Apr 2020

Scopus subject areas

  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Condensed Matter Physics

Fingerprint Dive into the research topics of 'Shape Memory Effects and Work Output of [001] Ni<sub>55</sub>Fe<sub>18</sub>Ga<sub>27</sub> Single Crystals in Torsion Mode'. Together they form a unique fingerprint.

Cite this