Kinetics of isothermal B2 → B19′ martensitic transformation in Ti49Ni51 shape memory alloy

N. Resnina, S. Belyaev, E. Demidova, Алексей Максимович Иванов, Владимир Александрович Андреев

Research output

6 Citations (Scopus)

Abstract

The B2 → B19′ martensitic transformation in a quenched Ni-rich NiTi alloy was found to proceed under isothermal conditions at temperatures both within and outside of the transformation temperature range as observed during continuous cooling measurement. The variation in the volume fraction of the martensite that appeared during isothermal holding of quenched Ni-rich NiTi alloy at different temperatures T was measured. It was found that the maximum volume fraction of the martensite (45%) appeared during holding at Ms temperature for 30 min. It was found that the kinetics of the isothermal transformation was different for T > Ms and T < Ms due to the different structure of the alloy before holding that might influence the mechanisms of the martensite formation.

Original languageEnglish
Pages (from-to)348-350
Number of pages3
JournalMaterials Letters
Volume228
DOIs
Publication statusPublished - 1 Oct 2018

Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Kinetics of isothermal B2 → B19′ martensitic transformation in Ti<sub>49</sub>Ni<sub>51</sub> shape memory alloy'. Together they form a unique fingerprint.

  • Cite this